Diamond Holographic Silver Foil
Name | Hot stamping foil |
Applicable Materials | ABS, PP, PE, PVC, PS, AS, PVC film, cosmetic plastics, glass bottles, aluminum ceilings, PU, artificial leather, acrylic and so on. |
Standard size | 640MM*120M/roll |
Other width specifications | 50CM、70CM、75CM、128CM 150CM |
Other length specifications | Split rolls according to customer requirements |
Thickness | 12um/15um |
Hot stamping temperature | 120°C-160°C |
Paper tube roll core | 120M-600M is one inch, 800M-2000M are three inches |
Packaging method | Regular carton, 10rolls/carton |
Carton Size/Weight | 65CM(L)*34CM(W)*14CM(H)，G.W.=16.5KG,N.W.16KG |
Color available | Gold, Silver ,red ,blue, green, iron gray ,black, matte , holographic, Etc |
Applications | Widely used in cosmetics PE hoses, bottles, lipstick tubes, electrical panels, decorative boards, stationery, pens, bottle caps, notebooks, football, toys, letters Card, shoe material, glass, etc |
Customized services | 1.Color 2.Size 3.Thickness |
MOQ | 10roll |
Method of delivery | Express Air Sea |
Delivery time | 3-15days FCL order within 25 days |
Payment method | XTransfer T/T |
Storage | Avoid humidity ,high temperature, sun exposure, vertical placement is more appropriate |
• Good coverage
• Excellent edgesharpness
• Applicable on a wide range of surfaces
•The adhesion performance is good, and the test can be passed
•Resistant to alcohol wiping
Sample service
Get samples of US$5.00/Piece!
Contact Supplier
Precautions
1. The appropriate series of hot stamping foil should be selected according to different materials, and great attention should be paid to the temperature, pressure and speed of the hot stamping process, and adjusted according to different materials and the size of the hot stamping area.
2. Electric aluminum foil has a vacuum aluminum coating, which is very sensitive to acids, alkalis and moisture, therefore, the paper, ink (especially black), dry paint and synthetic glue suitable for customers must be neutral. The finished print must be dry enough so as not to oxidize or damage the inner film layer）